Mechanical properties evaluation of metacarpophalangeal joint prosthesis with new titanium-nickel memory alloy: a
Minzheng Guo1,2, Baochuang Qi1,2, Jun Li2
1Kunming Medical University, 650500, Kunming, China.
Objective:
Ni-Ti memory alloys are unusual materials for hard-tissue replacement because of their unique superelasticity, good biocompatibility, high strength, low specific gravity, low magnetism, wear resistance, corrosion resistance and fatigue resistance. The current study aims to evaluate its mechanical properties and provide biomechanical basis for the clinical application of the prosthesis.
Methods:
Ten adult metacarpophalangeal joint specimens were randomly divided into a prosthesis group (n = 5, underwent metacarpophalangeal joint prosthesis) and a control group (n = 5, underwent sham operation). Firstly, the axial compression strength was tested with BOSE material testing machine to evaluate its biomechanical strength. Secondly, these specimens were tested for strain changes using BOSE material testing machine and GOM non-contact optical strain measurement system to evaluate the stress changes. Thirdly, fatigue test was performed between groups. Lastly, the mechanical wear of the metacarpophalangeal joint prosthesis was tested with ETK5510 material testing machine to study its mechanical properties.
Results:
Axial compression stiffness in the prosthesis group was greater than that in the control group in terms of 30 ° and 60 ° flexion positions (P < 0.05). There was no statistically significant difference between two groups with regards to axial compression stiffness and stress change test (P > 0.05). In the fatigue wear test, the mean mass loss in the prosthesis group's prosthesis was 17.2 mg and 17.619 mm3, respectively. The mean volume wear rate was 0.12%. There was no statistically significant difference in the maximum pull-out force of the metacarpal, phalangeal, and polymer polyethylene pads between the prosthesis group and the control group specimens.
Conclusions:
Ni-Ti memory alloy metacarpophalangeal joint prosthesis conforms to the biomechanical characteristics of metacarpophalangeal joints without implants, and the fatigue strength can fully meet the needs of metacarpophalangeal joint activities after joint replacement.