Tough and antibacterial poly(l-lactic acid) composites prepared via blending with the bifunctional macromolecular...

In order to expand the application of PLLA in the packaging field, improving its toughness and antibacterial activity has been widely concerned. However, seldom researches can simultaneously efficiently improve the toughness and antibacterial activity of PLLA by adding one kind of additions. To address above problems, the bifunctional branched poly(butylene adipate) ionomer additive (b-PBAUi) was synthesized. For b-PBAUi, its branched structure not only increased the plasticizing effect of additive, but also acted as reaction sites to introduce more antibacterial ionic salt. Due to the special structure of b-PBAUi, PLLA/b-PBAUi blends achieved excellent toughness and antibacterial efficiency. The elongation of blend reached 125 % even by adding 5 wt% b-PBAUi, which was 10 times higher than that of PLLA. From the analysis of phase morphology, it could be found that the microvoids promoting tensile yielding was the main tensile toughening mechanism for PLLA/b-PBAUi blends. In addition, the antibacterial activity of PLLA was significantly improved by adding b-PBAUi. For PLLA/b-PBAUi₁₀ and PLLA/b-PBAUi₁₅, the antibacterial efficiency against E. coli and S. aureus bacteria exceeded 99.0 %. By comprehensive consideration, the optimal blend ratio was achieved by PLLA/b-PBAUi₁₀ due to its excellent toughness and antibacterial efficiency.