Enhancing H₂O₂ utilization efficiency for catalytic wet peroxide oxidation through the doping of La in the Fe-ZSM-5...

Iron-loaded zeolite (Fe-zeolite) has shown great potential as an efficient catalyst for degrading organic pollutants with high concentrations in the catalytic wet peroxide oxidation (CWPO) process under mild conditions. Here, 0.4 wt% Lanthanum (La) was added in the 1.0 wt% Fe-ZSM-5 by two-step impregnation method for an enhanced H₂O₂ utilization efficiency. For a systematical comparison, the CWPO process at 55 °C, where m-cresol with a high concentration of 1000 mg/L as a substrate, was studied over Fe-ZSM-5 and Fe-La-ZSM-5 catalysts. Compared with Fe-ZSM-5, Fe-La-ZSM-5 showed 15% higher H₂O₂ utilization efficiency with comparable total organic carbon (TOC) removal at around 40%, meanwhile with a 15% reduced metal leaching. Transmission electron microscopy (TEM) with elemental mapping (EDS), surface acidity analysis by Fourier transform infrared (FT-IR) and NH₃-temperature programmed desorption (NH₃-TPD), redox property analysis by Raman spectroscopy and H₂-temperature-programmed reduction (H₂-TPR) of both catalysts revealed, that the La doped Fe-ZSM-5 can provide an altered surface acidity, a more uniform and evenly dispersed surface Fe species with a promoted reducibility, which effectively promoted the accurate decomposition of H₂O₂ into the reactive •OH radicals, enhanced the H₂O₂ utilization efficiency, and increased the catalyst stability. Also, more than 90% conversion was maintained during the continuous experiment for more than 10 consecutive test days under 55 °C without pH adjustment, showing a promising possibility of the Fe-La-ZSM-5 for a practical wastewater treatment process.