UV Dosage Unveils Toxic Properties of Weathered Commercial Bioplastic Bags

Previous studies indicated that weathered conventional plastics and bioplastics pose ecotoxicological risks. Here, the effects of artificial and natural weathering on the ecotoxicity of three compostable bags and a conventional polyethylene (PE) bag are investigated. With that aim, a 21-day artificial indoor weathering experiment featuring UV light, UV-filtered light, and darkness was run simultaneously to a 120-day outdoor littoral mesocosm exposure featuring natural light, UV-filtered light, and shaded conditions. Acute toxicity of so-weathered plastic specimens was tested in vivo using the sensitive Paracentrotus lividus sea-urchin embryo test. PE was nontoxic from the beginning and did not gain toxicity due to UV weathering. In contrast, for bioplastics, dry artificial UV weathering increased toxicity in comparison to the dark control. Weathering in outdoor mesocosm led to a rapid loss of toxic properties due to leaching in rainwater. With a higher UV dosage, a plastic-type-dependent regain of toxicity was observed, most likely driven by enhanced availability or transformation of functional additives or due to bioplastic degradation products. PE showed moderate UV absorbance, while bioplastics showed high UV absorbance. This study highlights the potential of biodegradable plastics to pose enhanced ecotoxicological risk due to weathering under environmentally relevant conditions.