Preparation and Degradation Performance Study of P(AM/GG/PEGDA) Nanocomposite Self-Degradation Gel Plugging Material

Lost circulation is a world-class problem, and the contradiction between plugging and unplugging in reservoirs is a problem that needs to be solved urgently. The traditional LCM is not suitable for reservoirs and the complex subsequent operations. Currently, a self-degrading plugging material is proposed. In this paper, a new self-degradation plugging material, CKS-DPPG, was prepared by AM, GG, nano silica, and PEGDA. The effects of reactant concentration, pH, mineralization, etc., on the swelling and degradation performance of CKS-DPPG were investigated. The plugging capacity was tested by fracture plugging equipment, and the mechanism of self-degradation was revealed. The results show that the CKS-DPPG reached a 50% degradation rate in 54 h and complete degradation in 106 h at 80 °C and pH = 8. Low temperatures, high mineralization, and weak alkaline conditions prolong the complete degradation time of CKS-DPPG, which facilitates subsequent operations. The simulation of the 3 mm opening fracture plugging experiment showed that the pressure-bearing capacity reached 6.85 MPa and that a 0.16 MPa pressure difference could unplug after degradation. The ester bond of PEGDA is hydrolyzed under high-temperature conditions, and the spatial three-dimensional structure of CKS-DPPG becomes linear. The CKS-DPPG can effectively reduce subsequent unplugging operations and lower production costs.