Fatigue Behaviour and Its Effect on the Residual Strength of Long-Fibre-Reinforced Thermoplastic PP LGF30

It is undeniable that mechanical properties, such as the stiffness or residual strength of fibre-reinforced thermoplastics, are adversely affected by fatigue damage caused by cyclic loading. In order to quantify and predict this damage influence, a calculation approach was developed in the past for the subgroup of short-fibre-reinforced thermoplastics. In order to test and expand the applicability of this approach to the field of long-fibre-reinforced thermoplastics, the decrease in mechanical properties is investigated experimentally in this paper using PP LGF30, propylene reinforced with long glass fibres, as an example. The paper describes both the fatigue behaviour and the residual strength of the material after fatigue damage. A decrease in the residual strength of up to about 35% could be recorded. The paper also presents a modelling approach that predicts the orientation-dependent fatigue strength of the material, and furthermore allows for the calculation of its residual strength as a function of fatigue damage. The novelty of the contribution lies in the continuous modelling of fatigue behaviour for arbitrary oriented samples of long-fibre-reinforced thermoplastics and also in the prediction of its residual strength depending on previously induced fatigue damage.