Simultaneous Multi-surface Anodizations and Stair-like Reverse Biases Detachment of Anodic Aluminum Oxides in Sulfuric and Oxalic Acid Electrolyte
10:27

Simultaneous Multi-surface Anodizations and Stair-like Reverse Biases Detachment of Anodic Aluminum Oxides in Sulfuric and Oxalic Acid Electrolyte

Published on: October 5, 2017

7.3K

Healable Anti-Corrosive and Wear-Resistant Silicone-Oil-Impregnated Porous Oxide Layer of Aluminum Alloy by Plasma

Yeji Shin1, Kichang Bae1, Sumin Lee1

  • 1Department of Metallurgical Engineering, Pukyong National University, Busan 48513, Republic of Korea.

Nanomaterials (Basel, Switzerland)
|September 28, 2023
PubMed

Keywords:
corrosion resistanceoil impregnationplasma electrolytic oxidationsilicone oilwear resistance

More Related Videos

Determining Tribocorrosion Rate and Wear-Corrosion Synergy of Bulk and Thin Film Aluminum Alloys07:12

Determining Tribocorrosion Rate and Wear-Corrosion Synergy of Bulk and Thin Film Aluminum Alloys

Published on: September 11, 2018

11.4K
The Effect of Anodization Parameters on the Aluminum Oxide Dielectric Layer of Thin-Film Transistors12:32

The Effect of Anodization Parameters on the Aluminum Oxide Dielectric Layer of Thin-Film Transistors

Published on: May 24, 2020

8.8K

Related Concept Videos

Corrosion02:49

Corrosion

The degradation of metals due to natural electrochemical processes is known as corrosion. Rust formation on iron, tarnishing of silver, and the blue-green patina that develops on copper are examples of corrosion. Corrosion involves the oxidation of metals. Sometimes it is protective, such as the oxidation of copper or aluminum, wherein a protective layer of metal oxide or its derivatives forms on the surface, protecting the underlying metal from further oxidation. In other cases, corrosion is...
Radical Autoxidation01:20

Radical Autoxidation

The oxidation of an organic compound in the presence of air or oxygen is called autoxidation. For example, cumene reacts with oxygen to form hydroperoxide. Autoxidation involves initiation, propagation, and termination steps. Many organic compounds are susceptible to autoxidation—especially ethers in the presence of oxygen, which form hydroperoxides. Even though this reaction is slow, old ether bottles contain small amounts of peroxide, which leads to laboratory explosions during ether...
Colloidal precipitates01:09

Colloidal precipitates

The high insolubility of some precipitates can result in an unfavorable relative supersaturation. This can lead to colloidal particles with a large surface-to-mass ratio, where adsorption is promoted. For instance, in the precipitation of silver chloride, silver ions are adsorbed on the surface of the colloidal particles, forming a primary layer. This layer attracts ions of opposite charge (such as nitrate ions), forming a diffuse secondary layer of adsorbed ions. This electric double layer...
Electrodeposition01:08

Electrodeposition

Electrodeposition is a technique used to separate an analyte from interferents by electrochemical processes. Here, the analyte is a metal ion that can be deposited on an electrode immersed in the sample solution. The electrochemical setup consists of an anode and a cathode. When an electric current is applied to the setup, oxidation occurs at the anode. At the cathode, which consists of a large metal surface, metal ions undergo reduction and deposit onto the surface.
Electrodeposition can...
Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
Microbial Corrosion01:24

Microbial Corrosion

Microbiologically Influenced Corrosion (MIC) is a significant form of material degradation caused by the metabolic activities of microorganisms. This phenomenon poses substantial challenges across various industries, including oil and gas, maritime, and water treatment sectors.MIC occurs when microorganisms, such as bacteria, archaea, and fungi, colonize metal surfaces, forming biofilms that alter the local electrochemical environment. These biofilms can lead to the production of corrosive...