Agarose fibers with glycerol and graphene oxide and functional properties for potential application in biomaterials

Agarose has numerous applications in biochemistry and medical textiles. This study aimed to produce agarose-graphene oxide-glycerol fibers and analyze their properties. The agarose gel was prepared by dissolving the polymer in 9:1 (v/v) dimethyl sulfoxide (DMSO): H₂O, followed by spinning in an ethanol bath (1:1 (v/v) ethanol: H₂O) at 20 °C. Fibers were obtained using 8 % (m/v) agarose, 2 % (m/v) glycerol, and 0.5 % and 1 % (m/v) graphene oxide (GO). The fibers had a titer of 18.32-32.49 tex and, a tenacity of 1.40-3.35 cN/tex. GO increased the thermal resistance by 79 %. The presence of glycerol and GO was confirmed and analyzed by FTIR and XPS. Fiber water absorption was decreased by 30 % with the GO addition. The weight loss increased by 55 % after glycerol addition, 51 % with GO addition, and 36 % with glycerol and GO simultaneous addition. Furthermore, GO exhibited 100 % inhibition for both S. aureus (gram-positive) and E. coli bacteria (gram-negative). Fiber F1, with only agarose, inhibited S. aureus by 34.93 %, F2 with 2 % glycerol by 48.72 %, F3 with 0.5 % GO by 63.42 %, and F4 with 2 % glycerol and 0.5 % GO by 30.65 %. However, the inhibition increased to 49.43 % with 1 % GO. The agarose fibers showed low inhibition for E. coli, ranging from 3.35 to 12.12 %.