Extraction of W, V, and As from spent SCR catalyst by alkali pressure leaching and the pressure leaching mechanism

Spent selective catalytic reduction (SCR) catalysts are environmentally hazardous and resource-enriching. In this work, V, W, and As in a spent SCR catalyst was extracted by alkali pressure leaching. Results showed that the V, W, and As were loaded on the anatase TiO₂ crystal grains as amorphous oxides. The optimum pressure leaching conditions were NaOH concentration of 20 wt%, reaction temperature of 180 °C, reaction time of 120 min, L/S of 10 mL/g, and stirring speed of 300 rpm. The leaching efficiency of W, V, and As reached 98.83%, 100%, and 100%, respectively. The experiment revealed the preferential leaching of V and As rather than W, and the leaching mechanisms of V, W, and As were studied through experiment and density functional theory (DFT). The leaching kinetics of W conformed to a variant of the shrinking core model and the leaching process of W is controlled by both chemical reactions and diffusion processes. During the leaching process, Na₂Ti₂O₄(OH)₂ product powder layer was generated, which affects the mass transfer of W. The destruction of the TiO₂ skeleton in the spent SCR catalyst is essential for adequate W extraction, especially for the extraction of W embedded in the TiO₂ lattice. The DFT simulation result indicated that the V and As loaded onto the TiO₂ support are easier to absorb hydroxide ions rather than W, and the leaching reaction energy of V and As was lower than W, As, and V has leaching priority over the leaching of W. Furthermore, an anatase TiO₂ photocatalyst with the {001} crystal surface exposed was successfully prepared from the alkali pressure leaching residue. This work provides theoretical support for the metal leaching and utilization of spent SCR catalysts via alkali pressure leaching.