Highly active nisin coated polycaprolactone electrospun fibers against both Staphylococcus aureus and Pseudomonas...

In this study, a wound dressing of electrospun polycaprolactone (PCL) fibers incorporating the antimicrobial peptide (AMP) nisin was fabricated. Nisin was physically adsorbed to the PCL fibers and tested for antibacterial activity against both Staphylococcus aureus (S. aureus) and Pseudomonas aeruginosa (P. aeruginosa). The PCL fibers had an average diameter of 1.16 μm ± 0.42 μm and no significant change in diameter occurred after nisin adsorption. X-ray photoelectron spectroscopy (XPS) analysis of the fibers detected nitrogen indicative of adsorbed nisin and the signal was used to quantify the levels of coverage on the fiber surfaces. In vitro nisin release studies showed a burst release profile with 80 % of the nisin being released from the fibers within 30 min. Air plasma pre-treatment of the PCL fibers to render them hydrophilic improved nisin loading and release. Antibacterial testing was performed using minimum inhibitory concentration (MIC) and surface attachment assays. The released nisin remained active against both Gram positive S. aureus and Gram negative P. aeruginosa, which has previously been difficult to achieve with single polymer fiber systems. Mammalian cell culture of the nisin coated fibers with L-929 mouse fibroblasts and human epidermal keratinocytes (HEKa) showed that the nisin did not have a significant effect on the biocompatibility of the PCL fibers. The results presented here demonstrate that the physical adsorption, which is a post-treatment, overcomes the potential limitations of harsh chemicals and fabrication conditions of electrospinning from organic solvents and provides a drug loading system having effective antibacterial properties in wound dressings.