Assessment of enamel surface roughness and hardness with metal and ceramic orthodontic brackets using different
Rahaf N Zawawi1, Naif A Almosa1
1Department of Pediatric Dentistry and Orthodontics, Division of Orthodontics College of Dentistry, King Saud University, Riyadh, Saudi Arabia.
Background:
This study aimed to evaluate enamel surface roughness and microhardness following the use of different bracket materials (metal or ceramic), etchants (total- and self-etchants), and adhesive systems (precoated or flash-free).
Method:
A total of 99 extracted human premolars were selected for the analysis. The surface roughness was first assessed (roughness control). One specimen from each subgroup was examined using a scanning electron microscope to illustrate the surface topography. Eighty-eight teeth were prepared using total- or self-etchants and bonded to precoated or flash-free adhesive metal or ceramic brackets. The remaining 11 specimens were not bonded to brackets (microhardness controls). The brackets were debonded after immersion in distilled water for 24 h. The specimens were again scanned for surface roughness and topography imaging. Finally, the microhardness was assessed using a micro-Vickers hardness test at a force of 200 g for 10 s.
Result:
An overall statistically significant increase in surface roughness and reduced surface microhardness were observed in all experimental groups when compared with those in the control groups. The etchant type was the only variable found to contribute to the measured surface properties, with increased roughness and reduced microhardness introduced by total-etching compared to those by self-etching.
Conclusion:
Orthodontic brackets introduced a significant increase in enamel surface roughness and reduce microhardness compared with untreated enamel, regardless of the bracket material, etchant type, and adhesive system. The etchant type was the only variable contributing to these changes, with total etching having a more pronounced effect.