Simultaneous Enhancement of Efficiency and Operational-Stability of Mesoscopic Perovskite Solar Cells via Interfacial...

The combined effects of compact TiO₂ (c-TiO₂ ) electron-transport layer (ETL) are investigated without and with mesoscopic TiO₂ (m-TiO₂ ) on top, and without and with an iodine-terminated silane self-assembled monolayer (SAM), on the mechanical behavior, opto-electronic properties, photovoltaic (PV) performance, and operational-stability of solar cells based on metal-halide perovskites (MHPs). The interfacial toughness increases almost threefold in going from c-TiO₂ without SAM to m-TiO₂ with SAM. This is attributed to the synergistic effect of the m-TiO₂ /MHP nanocomposite at the interface and the enhanced adhesion afforded by the iodine-terminated silane SAM. The combination of m-TiO₂ and SAM also offers a significant beneficial effect on the photocarriers extraction at the ETL/MHP interface, resulting in perovskite solar cells (PSCs) with power-conversion efficiency (PCE) of over 24% and 20% for 0.1 and 1 cm² active areas, respectively. These PSCs also have exceptionally long operational-stability lives: extrapolated T80 (duration at 80% initial PCE retained) is ≈18 000 and 10 000 h for 0.1 and 1 cm² active areas, respectively. Postmortem characterization and analyses of the operational-stability-tested PSCs are performed to elucidate the possible mechanisms responsible for the long operational-stability.