Effect of B₂O₃ on the Structure, Properties and Antibacterial Abilities of Sol-Gel-Derived TiO₂/TeO₂/B₂O₃ Powders

This paper studies the influence of B₂O₃ on the structure, properties and antibacterial abilities of sol-gel-derived TiO₂/TeO₂/B₂O₃ powders. Titanium(IV) butoxide, telluric(VI) acid and boric acid were used as precursors. Differences were observed in the degree of decomposition of Ti butoxide in the presence of H₃BO₃ and H₆TeO₆ acids. The phase transformations of the obtained gels in the temperature range of 200-700 °C were investigated by XRD. Composite materials containing an amorphous phase and different crystalline phases (metallic Te, α-TeO₂, anatase, rutile and TiTe₃O₈) were prepared. Heating at 400 °C indicated a crystalline-to-amorphous-phase ratio of approximately 3:1. The scanning electron microscopy (SEM) analysis showed the preparation of plate-like TiO₂ nanoparticles. The IR results showed that the short-range order of the amorphous phases that are part of the composite materials consists of TiO₆, BO₃, BO₄ and TeO₄ structural units. Free B₂O₃ was not detected in the investigated compositions which could be related to the better connectivity between the building units as compared to binary TiO₂/B₂O₃ compositions. The UV-Vis spectra of the investigated gels exhibited a red shift of the cut-off due to the presence of boron and tellurium units. The binary sample achieved the maximum photodegradation efficiency (94%) toward Malachite green dye under UV irradiation, whereas the ternary sample photoactivity was very low. The compositions exhibited promising antibacterial activity against E. coli NBIMCC K12 407.