Tribological Performance of Anti-Wear Coatings on Tools for Forming Aluminium Alloy Sheets Used for Producing...

Ensuring adequate reliability of the production process of packaging closures has made it necessary to study the effect of annealing and varnishing variants on the strength and structural properties of the stock material. As a test material, EN AW-5052-H28 aluminium alloy sheets with a thickness of 0.21 mm were used. The surface treatment of the test material involved varnishing the sheet metal surface using various varnishes and soaking the sheet metal. The coefficient of friction and the abrasion resistance of the coatings were determined using the T-21 ball-and-disc tribotester. The tested sheets were subjected to tribological analysis by the T-05 roller-block tribotester using countersamples made of Caldie and Sverker 21 tool steels. The results of the tests showed differences in mechanical and structural properties depending on the method of sample preparation. Based on the test results, significant differences in the adhesion of anti-wear coatings were found. The results revealed that the most favourable friction conditions are provided by the CrN coating. The (AlTi)N interlayer in the (AlTi)N/(AlCr)N coating adheres to the substrate over the entire tested area and no detachment from its surface was observed, which proves good bonding at the substrate/coating interface. The tested AlTiN/TiAlSiXN coating is characterised by a more homogeneous, compact microstructure compared to the (AlTi)N/(AlCr)N coating.