Performance Improvement and Microstructure Characterization of Cement-Stabilized Roadbase Materials Containing...

The proper reutilization of the phosphogypsum (PG) by-product derived from the production of phosphoric acid and recycled concrete aggregate (RCA) from waste concrete in roadbase materials is of great necessity and importance. This investigation tried seeking a new approach to reuse them to high quality, including turning PG into calcinated PG (CPG) via washing and calcination, as well as adopting sodium metasilicate nonahydrate (SMN) to strengthen the roadbase materials of cement-stabilized CPG and RCA. Upon the mix design, with a series of experiments including unconfined compressive strength, the wet-dry cycle, freeze-thaw cycle, and scanning electron microscopy, the comprehensive effects of PG treatment, the CPG to RCA mix ratio, SMN dosage, wet-dry cycle and freeze-thaw cycle on the road performance of roadbase materials were well evaluated, and the traffic bearing capacity and microstructure characteristics were also analyzed. The results demonstrate that the 7 d unconfined compressive strength of CPG/RCA roadbase materials can reach 5.34 MPa as the CPG and SMN dosage are 20% and 11%, respectively, which meets the requirements of an extremely and very heavy traffic grade. After five wet-dry cycles and freeze-thaw cycles, the resistance of the CPG/RCA roadbase materials to moisture and frost was significantly improved as 11% SMN was added. Meanwhile, SMN contributes to the reduction in crack width and densifies the microstructure of CPG/RCA roadbase materials. The research results can be used to provide new guidance for building more durable roadbase materials.