Bond strength between denture lining material and CAD-CAM denture base resin: A systematic review and meta-analysis
Ana Larisse Carneiro Pereira1, Cristhian Camilo Madrid Troconis2, Míria Rafaelli Souza Curinga1
1PhD Candidate, Department of Dentistry, Federal University of Rio Grande do Norte (UFRN), Natal, Brazil.
Statement Of Problem:
An effective bond between a denture lining material and the denture base resin is necessary for proper function. Regarding the new technologies for manufacturing denture bases, a systematic search of the literature on this topic is lacking.
Purpose:
The purpose of this systematic review and meta-analysis was to evaluate the bond strength between denture lining material and computer-aided design and computer-aided manufacturing (CAD-CAM) denture base resin (milled and 3-dimensionally printed) versus conventional denture base resin.
Material And Methods:
Electronic databases (PubMed/MEDLINE, Scopus, and Web of Science) were independently searched by 4 researchers for relevant studies published up to April 2023. The population, intervention, comparison, and outcome (PICO) question was: "Comparing conventional and CAD-CAM (milled and 3-dimensionally printed) denture base materials, which promote greater bond strength when associated with denture lining material?" A meta-analysis was performed based on mean ±standard deviation bond strength values between denture base resins and denture lining material with 95% confidence intervals.
Results:
Five in vitro studies were included. For bond strength, no difference was noted between conventional and milled denture base resin (confidence interval: -0.99 [-2.17 to 0.20]; heterogeneity: t2=0.57; Chi2:4.57; I2=78%; P=.10), and conventional resin had better values compared with those of 3-dimensionally (3D) printed (confidence interval: 3.03 [2.40-3.66]; heterogeneity: t2=0.00; Chi2:0.56; I2=0%; P<.001) when relined with soft materials. The milled denture base resin was better than the conventional (confidence interval: -0.85 [-1.33 to -0.38]; heterogeneity: Chi2:28.87; I2=93%; P<.001), with no difference between 3D printed and conventional (confidence interval: 0.18 [-4.23 to 4.59]; heterogeneity: t2=16.51; Chi2:130.99; I2=98%; P=.94) for hard liners.
Conclusions:
The bond strength between resins for milled CAD-CAM denture bases and denture lining material was similar to that of conventional denture base resin, regardless of the consistency of the denture lining material. The bond strength to 3D printed CAD-CAM resin was lower than that of the milled version.
Related Concept Videos
01:12Bonding and Strength of Aggregate
01:25Structure of Cadherins
01:17Mortar Properties
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
00:55Laminins are the Adhesive Proteins of Basal Lamina
In humans, the five forms of alpha chains are LAMA 1, LAMA 2, LAMA 3, LAMA 4, and LAMA 5. The four forms of beta chains are LAMB 1, LAMB 2, LAMB 3, and LAMB 4. The three forms of gamma...
02:40Chemical Bonds
Atoms participate in a chemical bond formation to acquire a completed valence-shell electron configuration similar to that of the noble gas nearest to it in atomic number. Ionic, covalent, and metallic bonds are some of the important types of chemical bonds. Bond energy and bond length determine the strength of a chemical bond.
Types of Chemical Bonds
An ionic bond is formed due to electrostatic attraction between cations and anions. Often, the ions are formed by the transfer of electrons...