A Novel Hydrophobic Polyimide Film with Sag Structure Derived from Multi-Hybrid Strategy

Polyimide (PI) film with hydrophilic greatly limits their application in the field of microelectronic device packaging. A novel hydrophobic PI film with sag structure and improved mechanical properties is prepared relying on the reaction between anhydride-terminated isocyanate-based polyimide (PIY) containing a seven-membered ring structure and the amino-terminated polyamide acid (PAA) via multi-hybrid strategy, this work named it as hybrid PI film and marked it as PI-PIY-X. PI-PIY-30 showed excellent hydrophobic properties, and the water contact angle could reach to 102°, which is 20% and 55% higher than simply PI film and PIY film, respectively. The water absorption is only 1.02%, with a decrease of 49% and 53% compared with PI and PIY. Due to that the degradation of seven-membered ring and generation of carbon dioxide led to the formation of sag structure, the size of sag structures is ≈16.84 and 534.55 nm for in-plane and out-plane direction, which are observed on surface of PI-PIY-30. Meanwhile, PI-PIY-30 possessed improved mechanical properties, and the tensile strength is 109.08 MPa, with 5% and more than 56% higher than that of pure PI and PIY film, showing greatly application prospects in the field of integrated circuit.