Reconfigurable Photonic Crystal Reversibly Exhibiting Single and Double Structural Colors

Unlike absorption-based colors of dyes and pigments, reflection-based colors of photonic crystals, so called "structural colors", are responsive to external stimuli, but can remain unfaded for over ten million years, and therefore regarded as a next-generation coloring mechanism. However, it is a challenge to rationally design the spectra of structural colors, where one structure gives only one reflection peak defined by Bragg's law, unlike those of absorption-based colors. Here, we report a reconfigurable photonic crystal that exhibits single-peak and double-peak structural colors. This photonic crystal is composed of a colloidal nanosheet in water, which spontaneously adopts a layered structure with single periodicity (407 nm). After a temperature-gradient treatment, the photonic crystal segregates into two regions with shrunken (385 nm) and expanded (448 nm) periodicities, and thus exhibits double reflection peaks that are blue- and red-shifted from the original one, respectively. Notably, the transition between the single-peak and double-peak states is reversible.