Interface Diffusion and Compatibility of (Ba,La)FeO_3-δ Perovskite Electrodes in Contact with Barium Zirconate and...

Ba_1-LaFeO_3-δ perovskites (BLF) capable of conducting electrons, protons, and oxygen ions are promising oxygen electrodes for efficient solid oxide cells (fuel cells or electrolyzers), an integral part of prospected large-scale power-to-gas energy storage systems. We investigated the compatibility of BLF with lanthanum content between 5 and 50%, in contact with oxide-ion-conducting Ce_0.8Gd_0.2O_2-δ and proton-conducting BaZr_0.825Y_0.175O_3-δ electrolytes, annealing the electrode-electrolyte bilayers at high temperature to simulate thermal stresses of fabrication and prolonged operation. By employing both bulk X-ray diffraction and synchrotron X-ray microspectroscopy, we present a space-resolved picture of the interaction between electrode and electrolyte as what concerns cation interdiffusion, exsolution, and phase stability. We found that the phase stability of BLF in contact with other phases is correlated with the Goldschmidt tolerance factor, in turn determined by the La/Ba ratio, and appropriate doping strategies with oversized cations (Zn²⁺, Y³⁺) could improve structural stability. While extensive reactivity and/or interdiffusion was often observed, we put forward that most products of interfacial reactions, including proton-conducting Ba(Ce,Gd)O_3-δ and mixed-conducting (Ba,La)(Fe,Zr,Y)O_3-δ, may not be very detrimental for practical cell operation.