Production of Ultrafine PVDF Nanofiber-/Nanonet-Based Air Filters via the Electroblowing Technique by Employing PEG as a Pore-Forming Agent

Particles with diameters smaller than 2.5 μm (PM_2.5) can penetrate the respiratory system and have negative impacts on human health. Filter media with a porous surface and nanofiber/nanonet structure demonstrate superior filtration performance compared to traditional nano- and microfiber-based filters. In this study, nanostructured filters were produced using the electroblowing method from solutions containing different ratios of poly(vinylidene fluoride) (PVDF) and polyethylene glycol (PEG) polymers for the first time. By increasing the water-soluble PEG ratio in PVDF/PEG blend nanofibers and employing a water bath treatment to the produced mat afterward, a more porous fibrous structure was obtained with a lower average fiber diameter. Notably, the removal of PEG from the PVDF/PEG (3-7) sample, which had the highest PEG content, exhibited clustered nanofiber-/nanonet-like structures with average diameters of 170 and 50 nm at the points where the fibers intersect. Although this process resulted in a slight decrease in the filtration efficiency (-1.3%), the significant reduction observed in pressure drop led to a 3.2% increase in the quality factor (QF). Additionally, by exploiting the polarizability of PVDF under an electric field, the filtration efficiency of the nanostructured PVDF filters enhanced with a ratio of 3.6% after corona discharge treatment leading to a 60% improvement in the QF. As a result, the PVDF/PEG (3-7) sample presented an impressive filtration efficiency of 99.57%, a pressure drop (ΔP) of 158 Pa, and a QF of 0.0345 Pa^-1.