Fluoride Release and Rechargeability of Poly(lactic acid) Composites with Glass Ionomer Cement

This study investigates the fluoride release, rechargeability and degradation behaviors of newly developed anticariogenic poly(lactic acid) (PLA) composites. The PLA composite with various concentrations (0%, 5%, 10%, 15% and 20% by weight) of glass ionomer cement (GIC) and sodium fluoride (NaF) were prepared using solvent casting method. The fluoride release, fluoride rechargeability and degradation behavior were evaluated. All experimental groups demonstrated fluoride-releasing ability. The highest level of fluoride ions released was found in PLA composite with sodium fluoride (PLA/NaF). Following the 28-day period, both groups showed a gradual reduction in fluoride ion released, ranging between 0.03 ± 0.01 and 0.53 ± 0.06 ppm, although remaining within the effective range for tooth remineralization. However, the rechargeability was only observed in PLA composite with GIC (PLA/GIC). Following an eight-week in vitro degradation test, all PLA/NaF groups displayed a significantly higher percentage of weight change and water absorption compared to the PLA/GIC and the control group. In SEM analysis, the formation of surface porosities was clearly noticed in all PLA/NaF. All specimens retained their structural integrity throughout the study. In conclusion, the newly developed PLA/GIC displays promising possibilities as an anticariogenic material. Furthermore, the rechargeability of these ions are repeatable, ensuring their long-term utility.