Weld Line Strength of Polyamide Fiberglass Composite at Different Processing Parameters in Injection Molding...

This study examines the impact of injection parameters on the weld line strength of the polyamide 6 and 30% fiberglass (PA6 + 30% FG) composite samples. The effects of filling time, packing time, packing pressure, melt temperature, and mold temperature on the ultimate tensile strength (UTS) and the elongation value of the weld line are investigated. The results reveal that the filling time factor has the lowest influence rate. On the contrary, the packing pressure has the most considerable value of UTS standard deviation, indicating that this factor has a high impact rate. The melt temperature factor has the highest elongation standard deviation, pointing out the strong impact of melt temperature on the elongation value. In reverse, the filling time factor has the lowest elongation standard deviation, showing the low impact of this factor on the elongation value. Increasing the mold temperature enhances the elongation value greatly because a higher temperature generates a better connection in the weld line area. Although the UTS value improves modestly when the mold temperature control system is used, the elongation result from the mold temperature parameter is better than expected. The UTS result from all parameters presents a minor deviation; therefore, it is lower than expected. The optimal strength result from artificial neural networks with genetic algorithm optimization is 85.1 MPa, which is higher than the best experiment result of 76.8 MPa. Scanning electron microscopy (SEM) results show that the interface between the fiberglass and the PA matrix has high adherence. The fracture surface is smooth, indicating that the PA6 + 30% FG composite sample has a high fragility level. The findings could help to increase the injection sample's weld line strength by optimizing the injection molding conditions.