Fabrication of the Fe-Doped Corona Schiff Base for Enhanced Microwave Absorption Performance

A corolla-shaped Schiff base polymer was synthesized from terephthalaldehyde (TPAD), glutaraldehyde (GA), and p-phenylenediamine (PPD) by block copolymerization, and Schiff base iron complexes were formed by doping with FeCl₃. The microscopic morphology, crystal structure, and elemental valence state were characterized by field emission scanning electron microscopy (FESEM), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). Comparing the change of conductivity before and after Fe³⁺ doping, it was found that the conductivity did not break away from the category of insulator, and the doped sample is a paramagnetic material. Morphological changes were observed by adjusting the ratio of GA to TPAD, and it was found that the corolla-like structure was most complete when the ratio of GA to TPAD was 2:1, and its Schiff base iron complex absorbed waves better. At a thickness of 3 mm, the absorption effect can reach below -10 dB at 12.44-15.16 GHz, and the maximum absorption value is -45.07 dB at a thickness of 3.8 mm; it is an organic absorbing agent with excellent impedance matching and absorbing properties.