Degradation of bisphenol A by persulfate activation of MoS₂ composite iron tailings

In this paper, molybdenum disulfide was grown on the surface of iron-containing tailings by hydrothermal method, and a series of highly efficient activated persulfate (PMS) iron-based catalysts were successfully prepared. The results show that in the CTM 1-200/PMS system, the additional ratio of tailings and the hydrothermal temperature have important effects on the catalyst. The catalyst prepared under the conditions of CT:MoS₂ (molar ratio 1:1) and hydrothermal temperature of 200 °C (CTM 1-200) had the best degradation effect on BPA, and the degradation effect was increased by four times. The reason for the improvement of degradation efficiency is that the introduction of MoS₂ accelerates the REDOX cycle between Fe(II)/Fe(III), and the reduction of Fe(III) is mainly related to Mo(IV), while the reduction capacity of S is relatively weak. Molybdenum disulfide/iron tailing composite material provides a way for tailings to solve the problem of water pollution.