Fracture resistance and bonding performance after antioxidants pre-treatment in non-vital and bleached teeth

This study aimed to evaluate the effect of antioxidant solutions on fracture strength and bonding performance in non-vital and bleached (38% hydrogen peroxide) teeth. One hundred and eighty dentin specimens were obtained, 60 for each test: fracture strength, hybrid layer thickness, and bond strength. The groups (n=10) were randomly composed according to post-bleaching protocol: REST - restoration, without bleaching; BL - bleaching + restoration; SA - bleaching, 10% sodium ascorbate solution, and restoration; AT - bleaching, 10% α-tocopherol solution, and restoration; CRAN - bleaching, 5% cranberry solution, and restoration; CAP - bleaching, 0.0025% capsaicin solution, and restoration. Data were analyzed with ANOVA, Kruskal-Wallis, Dunn, and Qui-Square tests (α=0.05). The highest fracture strength values were observed in REST (1508.96 ±148.15 N), without significant difference for the bleached groups (p>0.05), regardless of the antioxidant use. The hybrid layer thickness in the group that was not subjected to bleaching (REST) was significantly higher than in any other group. The bond strength in the bleached and antioxidants-treated groups (SA, AT, CRAN, CAP) has no differences with the bleached group without antioxidants (BL). Adhesive failures were predominant in the groups that did not receive the antioxidant application. In conclusion, the evaluated antioxidants did not show an effect on the fracture strength, hybrid layer thickness, or bond strength of dentin bleached after endodontic treatment. The application of 10% sodium ascorbate, 10% alpha-tocopherol, 5% cranberry, or 0.0025% capsaicin solutions is not an effective step and should not be considered for the restorative protocols after non-vital bleaching.