Novel low-shrinkage dental resin containing microcapsules with antibacterial and self-healing properties

Dental resin restorations commonly fail because of fractures and secondary caries. The aim of this research was to synthesize a novel low-shrinkage dental resin with antibacterial and self-healing properties. The low-shrinkage dental resin was obtained by incorporating a 20 wt% anti-shrinkage mixture of an expanding monomer 3,9-diethyl-3,9-dimethylol -1,5,7,11-tetraoxaspiro[5,5] undecane and an epoxy resin monomer diallyl bisphenol A diglycidyl ether (1:1, referred as "UE") and different mass fractions of self-healing antibacterial microcapsules (0%, 2.5%, 5%, 7.5%, and 10%) were incorporated into the matrix to prepare multifunctional dental resin. Polymerization shrinkage, mechanical properties, antibacterial activity, self-healing ability, and cytotoxicity of this dental resin were evaluated. The polymerization volumetric shrinkage of resin containing 20 wt% UE and 7.5 wt% microcapsules was reduced by 30.12% (4.13% ± 0.42%) compared with control. Furthermore, it exhibited high antibacterial activity and a good self-healing efficiency of 71% without adversely affecting the mechanical property and cell viability. This novel multifunctional dental resin with low polymerization shrinkage and excellent antibacterial activity and self-healing capability has potential application as a dental resin material to decrease the incidence of fractures and secondary caries.