Multifunctional Acetamide Additive Combined with LiNO3 Co-Assists Low-Concentration Electrolyte Interfacial Stability
Yongchao Liu1, Jirui Wang1, Shengge Rong2
1School of Materials Science and Engineering, Anhui Provincial Key Laboratory of Advanced Functional Materials and Devices, Hefei University of Technology, Hefei, Anhui 230009, P. R. China.
Abstract:
Lithium metal batteries (LMBs) are expected to upgrade their energy density to meet the growing battery market demand; however, intractable lithium dendrites and prominent electrode-electrolyte interface problems have been the stumbling block to their practical applications. Electrolytes play a crucial role in LMBs and are directly involved in the establishment of the electrode-electrolyte interface. In particular, low-concentration electrolytes (LCEs) can significantly save electrolyte costs, but the interface issue is more noteworthy. Here, multifunctional acetamide (N-methyl-N-(trimethylsilyl)-trifluoroacetamide, MTA) and lithium nitrate (LiNO3) additives were introduced together to enhance the performance of LMBs in LCEs. The MTA additive effectively removes the trace water and corrosive HF from the electrolyte, thus suppressing lithium salt decomposition and enhancing the stability of LCEs. Moreover, the MTA additive can construct an inorganic-rich interphase layer on the cathode/anode surface to protect the electrode. Especially, MTA can cooperate with LiNO3 additive to suppress lithium dendrites and reduce interfacial impedance, thus effectively enhancing lithium metal anode stability. Benefiting from the introduction of MTA and LiNO3 additives in the LCEs, the Li||NMC811 metal battery still has a capacity of 110 mA h g-1 after 500 cycles at room temperature, while the reference batteries have failed. The rate capacity and high temperature (50 °C) performance of the Li||NCM811 batteries have also been significantly improved. Significantly, this research explores a cost-effective method of using multifunctional additives to enhance LMBs' stability in LCEs.
Related Concept Videos
01:20Amides to Amines: LiAlH4 Reduction
Amide reduction requires two equivalents of the reducing agent, acting as a source of hydride ions. As shown in the figure, the reaction is initiated with a nucleophilic attack by the hydride ion at the carbonyl carbon to form a tetrahedral intermediate.
01:20Anionic Chain-Growth Polymerization: Overview
01:19Acid Halides to Alcohols: LiAlH4 Reduction
The mechanism proceeds in three steps. First, the nucleophilic hydride ion attacks the carbonyl carbon of the acid halide to form a tetrahedral intermediate. Next, the carbonyl group is re-formed, and the halide ion departs as a leaving group, generating an aldehyde. A second nucleophilic attack by the hydride yields an alkoxide ion, which, upon protonation, gives a primary alcohol as...
00:55Nitriles to Amines: LiAlH4 Reduction
As shown below, the mechanism involves three steps. Firstly, the hydride ion acting as a nucleophile attacks the nitrile carbon to form an anion. In the second step, a second equivalent of the hydride ion attacks the anion to...
02:42Acidity of 1-Alkynes
The acidic strength of hydrocarbons follows the order: Alkynes > Alkenes > Alkanes. The strength of an acid is commonly expressed in units of pKa — the lower the pKa, the stronger the acid. Among the hydrocarbons, terminal alkynes have lower pKa values and are, therefore, more acidic. For example, the pKa values for ethane, ethene, and acetylene are 51, 44, and 25, respectively, as shown here.
01:14Acid Halides to Ketones: Gilman Reagent
As shown below, the mechanism proceeds in two steps. First, one of the alkyl groups of the reagent acts as a nucleophile and attacks the acyl carbon of the acid chloride to form a tetrahedral intermediate. This is followed by the reformation of the carbon–oxygen...