Influence of light exposure techniques on in vitro pulp temperature rise during bulk fill composite Class I...

This in vitro study assessed peak temperature and temperature increase (ΔT) within the pulp chamber during different extended photoactivation techniques (EPT-applying similar radiant exposure values) to resin-based composites (RBCs) placed in a Class I cavity preparation in an extracted human lower third molar. A T-type thermocouple was placed in the pulp chamber and connected to a temperature analysis device (Thermes, Physitemp). The tooth was attached to an assembly simulating the in vivo environment (controlled baseline pulp chamber temperature and fluid flow). The real-time pulp chamber temperature was evaluated throughout the photoactivation (Bluephase N, Ivoclar Vivadent) of two bulk-fill RBCs: Tetric N Ceram Bulk Fill (TBF; shade: IVA; Ivoclar Vivadent); Surefill SDR flow + (SDR, shade: Universal; Dentsply Sirona), which were exposed to different curing techniques: 40 s-occlusal surface; 20 s-occlusal + 10 s-buccal + 10 s-lingual surfaces; 10 s-buccal + 10 s + lingual + 20 s-occlusal surfaces. Each EPT delivered 42.4 J/cm². Vickers hardness (VHN) was measured on the removed, sectioned RBC restorations at the top and bottom middle areas after curing. ΔT and VHN data were analyzed using 2-way ANOVA followed by Bonferroni post-hoc test (α = 0.05). Peak temperature data were analyzed using one-way ANOVA and Dunnett's post-hoc test (α = 0.05). SDR showed higher ΔT values than TBF (p = 0.008) in some EPTs. Neither technique resulted in ΔT values greater than 5.5 °C. Both composites had acceptable bottom/top hardness ratios (greater than 80%), regardless of the photoactivation technique. The evaluated EPTs may be considered safe as a low-temperature increase was noticed within the pulp chamber.