Emulsion template fabricated gelatin-based scaffold functionalized by dialdehyde starch complex with antibacterial...

Gelatin and starch are considered as promising sustainable materials for their abundant production and good biodegradability. Efforts have been made to explore their medical application. Herein, scaffolds based on gelatin and starch with a preferred microstructure and antibacterial antioxidant property were fabricated by the emulsion template method. The dialdehyde starch was firstly combined with silver nanoparticles and curcumin to carry out the efficient hybrid antibacterial agent. Then, the gelatin microsphere of appropriate size was prepared by emulsification and gathered by the above agent to obtain gelatin-based scaffolds. The prepared scaffolds showed porous microstructures with high porosity of over 74 % and the preferred pore sizes of ∼65 μm, which is conducive to skin regeneration. Moreover, the scaffolds possessed a good swelling ability of over 640 %, good degradability of over 18 days, excellent blood compatibility, and cell compatibility. The promising antibacterial and antioxidant properties came from the hybrid antibacterial agent were affirmed. As expected, the gelatin-based scaffolds fabricated by the emulsion template method with a preferred microstructure can facilitate more adhered fibroblasts. In summary, gelatin-based scaffolds functionalized by starch-based complex expanded the application of abundant sustainable materials in the biomedical field, especially as antibacterial antioxidant wound dressings.