Fucoidan/collagen composite coating on magnesium alloy for better corrosion resistance and pro-endothelialization
Yahui Wang1, Yuan Zhao1, Xinyu Wang1
1School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450001, China; Henan Key Laboratory of Advanced Magnesium Alloys, Zhengzhou 450002, China.
Abstract:
Magnesium alloy stents (MAS) have broad application prospects in the treatment of cardiovascular diseases. However, poor corrosion resistance and biocompatibility greatly limit the clinical application of MAS. In this work, the coating consisting of MgF2 layer, polydopamine layer, fucoidan and collagen IV was constructed on Mg-Zn-Y-Nd (ZE21B) alloy to improve its corrosion resistance and pro-endothelialization potential. The fucoidan and collagen IV in the coating could obviously enhance the hemocompatibility and pro-endothelialization potential respectively. Compared with bare ZE21B alloy, the fucoidan/collagen composite coating modified ZE21B alloy possessed lower corrosion current density and better corrosion resistance. Moreover, the modified ZE21B alloy exhibited relatively low hemolysis rate, fibrinogen adsorption and platelet adhesion in the blood experiments, suggesting the improved hemocompatibility. Furthermore, the modified ZE21B alloy favorably supported the adhesion and proliferation of vascular endothelial cells (ECs) and effectively regulated the phenotype of smooth muscle cells (SMCs), thus improving the pro-endothelialization potential of vascular stent materials. The fucoidan/collagen composite coating can significantly improve the corrosion resistance and pro-endothelialization potential of ZE21B alloy, showing great potential in the development of degradable MAS.