The in situ phosphorization inducing oxygen vacancies in the core-shell structured NiFe oxides boosts the...

Transition metal-based oxides have been reported as an important family of electrocatalysts for water splitting owing to their possible large-scale applications that are highly desirable for the hydrogen generation industry. Herein, we report a facile method for the preparation of phosphate-decorated NiFe oxides on nickel foam as efficient oxygen evolution reaction (OER) electrocatalysts for water oxidation. The OER electrocatalysts were developed through the pyrolysis of MIL(Fe) metal-organic frameworks (MOFs), which were modified with Ni and P species. It was found that the formation of NiO on the Fe₂O₃ surface (NiO@Fe₂O₃) can enrich electrocatalytic active sites for the OER. Meanwhile, the incorporation of P into NiO@Fe₂O₃ (P-NiO@Fe₂O₃) creates abundant oxygen vacancies, which facilitates the surface charge transfer for OER electrocatalysis. Benefiting from the structure and composition advantages, P_2.0-NiO@Fe₂O₃/NF exhibits the best performance for OER electrocatalysis among other prepared electrocatalysts, with an overpotential of 208 mV at the OER current density of 10 mA cm^-2 and a small Tafel slope of 69.64 mV dec^-1 in 1 M KOH solution. Additionally, P_2.0-NiO@Fe₂O₃/NF shows an outstanding durability for the OER electrocatalysis, maintaining the OER current density above 20 mA cm^-2 for more than 100 h.