Non-iridescent Structurally Colored Pigments Based on CB@SiO₂@TiO₂ Core-Bishell Nanospheres with Enhanced Color...

In recent years, artificial amorphous photonic structure (APS) materials with high color saturation and angle independence have been competitively reported. However, there is a lack of research into their functionalization and application in practical environments. Here, with practical applications in mind, we prepared APS pigments based on CB@SiO₂@TiO₂ core-bishell nanospheres and demonstrated high color saturation, enhanced color stability, and excellent photocatalytic activity. SiO₂ effectively protected the carbon black particles from ablation during the calcination process. Paints composed of ethanol, ethyl cellulose (EC), and pigments could be spray-coated on any substrate to prepare a structurally colored coating without limitation. The coatings show good mechanical stability and photothermal stability. The color of the structurally colored pigments can be easily changed by adjusting the sizes of the CB@SiO₂@TiO₂ nanospheres. The photocatalytic activity of the pigments on formaldehyde (HCHO) and methylene blue (MB) solution and reaction kinetics of their degradation were studied by experiment. The results showed that the photocatalytic activity of the pigments increased with the increase of the TiO₂ loading, and the degradation rate of HCHO reached 96.7% for 3 h and that of MB reached 97.9% for 60 min when the TiO₂ shell thickness was 40 nm. The structurally colored pigments based on CB@SiO₂@TiO₂ nanospheres effectively solve the environmental problems caused by the application of pigments and have a promising future in the fields of color decoration, display, and painting.