Grain-growth Inhibitor with Three-section-sintering for Highly Dispersed Single-crystal NCM90 Cubes

Single crystallization of LiNi_x Co_y Mn_1-x-y O₂ (NCM) is currently an effective strategy to improve the cycling life of NCM cathode, owing to the reduced surface area and enhanced mechanical strength, but the application of single crystal NCM(SC-NCM) is being hindered by severe particle agglomeration and poor C-rate performance. Here, a strategy of three-section-sintering(TSS) with the presence of grain-growth inhibitor was proposed, in which, the TSS includes three sections of phase-formation, grain-growth and phase-preservation. While, the addition of MoO₃ inhibits the grain growth and restrains the particle agglomeration. With the help of TSS and 1 mol % of MoO₃ , highly dispersed surface Mo-doped SC-NCM(MSC-NCM) cubes are obtained with the average diameter of 1.3 μm. Benefiting from the surface Mo-doping and the reduced surface energy, the Li⁺ -migration preferred (1 0 4) crystalline facet is exposed as the dominant plane in MSC-NCM cubes, because of which, C-rate performance is significantly improved compared with the regular SC-NCM. Furthermore, this preparation strategy is compatible well with the current industrial production line, providing an easy way for the large-scale production of SC-NCM.