Nondestructive volumetric optical analysis of corroded copper oxidation using 1700nm swept-source optical coherence...

This study presents a novel nondestructive analysis method for precise characterization of corroded copper oxidation using optical coherence microscopy (OCM). By exploiting the partial light transmission through metallic oxide layers, we employed a specialized OCM system with a wavelength of 1700nm and enhanced the analysis accuracy compared to conventional optical coherence tomography (OCT). The developed OCM system featured a numerical aperture (NA) of 0.15, providing improved surface profiling and higher lateral resolution than OCT. we developed a peak-finding algorithm to accurately determine the thickness of the copper oxide layer from the acquired interference data with zero padding. Our method was validated by comparing the measured thickness profiles with those obtained from scanning electron microscope (SEM) images of corroded metals. The copper oxidation specimens were prepared after heat treatment for 1, 2, 4, and 8 h in an alumina tube furnace at a temperature of 900 °C to find the correlation between the OCM thickness measurement. Additionally, the acquired enface 3D images enabled the identification of local corrosion distribution within a 4 mm × 4 mm area. The en-face mapping images are utilized to analyze the uniformity of the metal oxidation process across the imaging area of the copper oxidation specimens. With an increase in heat treatment time, the median value of the thickness histogram for the copper oxide within the area consistently remained around 10 µm. However, the thickness variation ranged from -2 µm to 5 µm. This indicates that as the heat treatment time progresses, the thickness of the copper oxide becomes more non-uniform. Our technique holds great potential for nondestructive and noncontact detection of metal corrosion and assessment of corrosion rates in various industrial applications. Future research efforts could focus on expanding the application of OCM to different metals and exploring its commercialization prospects for practical implementation in diverse industries.