Rb(Zn,Cu)₄As₃ as a New High-Efficiency Thermoelectric Material

The thermoelectric performance of RbZn_4-CuAs₃ crystallized in the KCu₄S₃-type structure was investigated. Samples were synthesized via solid-state reactions, followed by hot pressing. Hole carriers were doped by substituting Zn with Cu until x = 0.02, resulting in an increase of the power factor from 0.049 to 0.52 mW/mK² at T = 797 K. The lattice thermal conductivity was substantially low, with a value of 1.61 W/mK at T = 312 K, independent of doping. This can be attributed to the large vibration of the Rb atoms, as demonstrated by the neutron diffraction analysis. The maximum dimensionless figure of merit, ZT, was 0.53 at T = 797 K, representing the highest value for the 143-Zintl compounds. The result indicated that the 143-Zintl compounds could be a new class of high-performance thermoelectric materials.