A novel yttrium stabilized zirconia and ceria composite electrolyte lowering solid oxide fuel cells working...

Reducing the working temperature and improving the ionic conductivity of electrolytes have been the critical challenges for the gradual development of solid oxide fuel cells (SOFCs) in practical applications. The researchers all over the world attempt to develop alternative electrolyte materials with sufficient ionic conductivity. In this work, YSZ-CeO₂ composite material was used as electrolytes in the construction of symmetrical SOFCs. The maximum power densities (P_max) of YSZ-CeO₂ based fuel cell can reach 680 mW cm^-2 at 450 °C, 510 mW cm^-2 at 430 °C, 330 mW cm^-2 at 410 °C and even 200 mW cm^-2 as the operational temperature was reduced to 390 °C. A series of characterizations indicates that the activation energy of the YSZ-CeO₂ composite is significantly decreased, and the enhancement effect for ion conduction comes from interface transport. Our findings indicate the YSZ-CeO₂ composite material can be a highly promising candidate for advanced low-temperature SOFC.