Assessment of Nanoscale Configuration of Dentin in Non-carious Cervical Lesions

Introduction Non-carious cervical lesions (NCCLs) are structural deformities or tissue loss in the cervical region of teeth, which are closer to the gum line that do not result from caries (tooth decay). On the tooth enamel at the gingival margin, these lesions are frequently seen as V- or U-shaped notches. The causes of NCCLs are multifaceted and involve intricate relationships between chemical, mechanical, and biological elements. The slow loss of enamel and dentin in the cervical area occurs due to mechanical causes like abrasive toothbrushing and occlusal tension, as well as chemical variables such as erosive acidic food components. As NCCLs advance, dental discomfort, aesthetic issues, and impaired tooth function may result. The aim of this study was to assess the nanoscale configuration of dentin in non-carious cervical lesions using scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS). Methodology Sterilized teeth samples were selected from the extracted tooth repository of Saveetha Dental College and Hospitals, Chennai. Tooth samples were thinly sliced using a diamond bur. The sliced teeth were examined using a scanning electron microscope. Ionic configuration was assessed using EDS and elemental analysis. Results The findings showed the nanoscale morphology and elemental configurations present. Elemental mapping showed specific elemental localization in the affected area. Conclusion NCCLs can be attributed as a predominant factor leading to gingival recession causing dentin exposure and hypersensitivity. NCCLs can also threaten the integrity of dentin; therefore, early diagnosis of non-carious cervical lesions is crucial to ensure proper treatment plan and therapeutic regimens.