Investigation of tribo-mechanical performance of alkali treated rice-husk and polypropylene-random-copolymer based...

This study was based on the experimental performance evaluation of a wood polymer composite (WPC) that was synthesized by incorporating untreated and treated rice husk (RH) fibers into a polypropylene random copolymer matrix. The submicron-scale RH fibers were alkali-treated to modify the surface and introduce new functional groups in the WPC. A compatibilizer (maleic anhydride) and a thermos-mechanical properties modifier (polypropylene grafted with 30 % glass fiber) were used in the WPC. The effects of untreated and treated RH on the WPC panels were studied using FESEM, FTIR, and microscope images. A pin-on-disk setup was used to investigate the bulk tribological properties of PPRC and WPC. The complex relationship between the friction coefficient of different loading of RH fibers in the WPC, as a function of sliding distance, was analyzed along with the temperature and morphology of the surface. It was observed that untreated RH acted as a friction modifier, while treated RH acted as a solid lubricant. Microhardness was calculated using the QCSM module on nanoindentation. It was found that untreated RH led to an increase in microhardness, while treated RH caused a decrease in hardness compared to PPRC.