Engineering Phase to Reinforce Dielectric Polarization in Nickel Sulfide Heterostructure for Electromagnetic Wave...

Engineering phase transition in micro-nanomaterials to optimize the dielectric properties and further enhance the electromagnetic microwave absorption (EMA) performance is highly desirable. However, the severe synthesis conditions restrict the design of EMA materials featuring controllable phases, which hinders the tunability of effective absorption bandwidth (EAB) and leads to an unclear loss mechanism. Herein, a seed phase decomposition-controlled strategy is proposed to induct nickel sulfide (NiS_x) absorbers with controllable phases and hollow sphere nature. Transmission electron microscopy holography and theoretical calculations evidence that the reconstruction of atoms in phase transition induces numerous heterogeneous interfaces and lattice defects/sulfur vacancies to cause varied work functions and local electronic redistribution, which contributes to reinforced dielectric polarization. As a result, the optimized NiS₂/NiS heterostructure enables enhanced EM attenuation capability with a wide EAB of 5.04 GHz at only 1.6 mm, compared to that of NiS₂ and NiS. Moreover, the correlation between EAB and NiS phase content is demonstrated as the "volcano" feature. This study on the concept of phase transition of micro-nanomaterials can offer a novel approach to constructing highly efficient absorbers for EMA and other functionalities.