Effective electronic waste valorization via microwave-assisted pyrolysis: investigation of graphite susceptor and...

Waste printed circuit board (WPCB) was subjected to microwave-assisted pyrolysis (MAP) to investigate the energy and pyrolysis products. In MAP, pyrolysis experiments were conducted, and the effects of WPCB to graphite mass ratio on three-phase product yields and their compositions were analyzed. In addition, the role of the initial WPCB mass (10, 55, and 100 g) and susceptor loading (2, 22, and 38 g) on the quality of product yield was also evaluated. By using design of experiments, the effects of graphite susceptor addition and WPCB feedstock quantity was investigated. A significant liquid yield of 38.2 wt.% was achieved at 38 g of graphite and 100 g of WPCB. Several other operating parameters, including average heating rate, pyrolysis time, microwave energy consumption, specific microwave power used, and product yields, were optimized for the MAP of WPCB. Pyrolysis index (PI) was calculated at the blending of fixed quantity WPCB (100 g) and various graphite quantities in the following order: 2 g (21) > 20 g (20.4) > 38 g (19.5). The PI improved by increasing the WPCB quantity (10, 55, and 100 g) with a fixed quantity of graphite. This work proposes the product formation and new reaction pathways of the condensable compounds. GC-MS of the liquid fraction from the MAP of WPCBs without susceptor resulted in the generation of phenolic with 46.1% relative composition. The addition of graphite susceptor aided in the formation of phenolic and the relative composition of phenolics was found to be 83.6%. The area percent of phenol increased from 42.8% (without susceptor) to 78.6% (with susceptor). Without a susceptor, cyclopentadiene derivative was observed in a very high composition (~ 31 area %).