Strong and ultrafast stimulus-healable lignin-based composite elastomers with excellent adhesion properties

With the increased environmental issues, advanced high-performance and multifunctional polymeric materials derived from biomass have tremendous attention due to the great potential to replace their traditional petroleum-based counterparts. In this work, a series of lignin graft copolymers, lignin-graft-poly(n-butyl acrylate-co-acrylic acid) (Lig-g-P(BA-co-AA)), were rationally prepared via reversible addition-fragmentation chain transfer (RAFT) polymerization. These lignin-based copolymers demonstrate good thermal stability and tunable glass transition temperature (T_g) values. The mechanical performance, including tensile strength, extensibility, Young's modulus, and toughness can be facilely adjusted by the BA/AA feed ratio and lignin content during polymerization. Owing to the extraordinary photothermal conversion ability of lignin, the Lig-B₅₅₀ copolymer, containing 11.8 wt% lignin content, shows excellent stimulus-healing behavior within 1 min with a 97.1 % healing efficiency under near-infrared (NIR) laser irradiation. Moreover, the Lig-g-P(BA-co-AA) copolymers exhibit remarkable adhesion property, broadening their potential applications in the adhesive area. This grafting strategy is versatile and efficient, conferring the resultant lignin-based composite elastomers with dramatically enhanced mechanical properties and unprecedented photothermal behavior, which can inspire the further development of strong lignin-based sustainable elastomers.