A novel method for effective solidifying chromium and preparing crude stainless steel from multi-metallic...

Electroplating sludge (ES) is a globally prevalent hazardous waste that primarily contains Cr, Cu, Ni, and Fe. However, the residual Cr phases within the slag potentially poses an environmental risk in current vitrification. A novel method for effective recovering and solidifying Cr in ES is proposed in this work. ES was desulfurized and subsequently co-treated with ferrosilicon (Fe-Si) and spent carbon anode (SCA) for enhancing the recovery of Cr, Cu, Ni, and Fe to prepare crude stainless steel. Under optimal conditions, the recovery ratios of Cr, Cu, Ni, and Fe reached 96.96%, 99.45%, 99.92%, and 99.20%, respectively, signifying improvements of 21.4%, 0.2%, 1.5%, and 2.8%, respectively, compared with existing research. Meanwhile, the fluoride in SCA yielded CaF₂, further progressing to the Si-Ca-F-Na-Al-O phase, with a solidification ratio of 97.87%. The Cr leaching content of the residual Cr-Cu-S phase in the slag remained below 5 mg/L across a pH range of 2-4, demonstrating enhanced stability compared to prior alloy, oxide, and chemically dissolved phases. An innovative approach for solidify Cr by forming matte holds implications for the treatment of Cr-containing solid wastes such as chromium slag, tannery sludge and stainless steel slag.