Advanced Marine Antifouling Hydrogels Based on 7-Amino-4-methylcoumarin Fluorescence Driven by Rare-Earth
Qitong Mao1, Siqi Liu1, Yangkai Xiong1
1State Key Laboratory of Marine Resource Utilization in South China Sea, School of Materials Science and Engineering, Hainan University, Haikou 570228, China.
Abstract:
At present, there are very few reports on the combination of phosphorescence and fluorescence in the field of pollution prevention. A composite antibacterial agent was designed to store energy by using the phosphorescence effect of rare earth oxides, emit light at night, and stimulate 7-amino-4-methylcoumarin to produce fluorescence and prevent algae from adhering. When complexed with PVA, it exhibited excellent characteristics as an all-weather autocatalytic phosphorescence-fluorescence antifouling hydrogel. The rare earth phosphorescent powder was prepared in a high-temperature tube furnace, coated with SiO2 on the surface for waterproofing, and then grafted with 7-amino-4-methylcoumarin to obtain a composite antibacterial agent with a phosphorescence-fluorescence effect. The composite antibacterial agent was added with PVA to obtain a hydrogel, which exhibited bactericidal rates of more than 99.98% against both Gram-positive and Gram-negative bacteria after 48 h. The results of fluorescence staining showed that the coverage rate of dead bacteria reached 41.6% after 24 h. The tensile strength of the antifouling hydrogel is up to 1.49 MPa, which is strong enough for real marine environments. Moreover, the algae coverage area of the composite hydrogel under natural light was only 2.7%, representing a 10-fold reduction compared with the control. The antifouling hydrogel has good antipollution and algae suppression performance, which is due to the fact that the rare earth phosphorescent powder when exposed to sunlight can provide a light source to stimulate 7-amino-4-methylcoumarin fluorescence at night and thereby prevent algae adhesion. After testing in the marine field and the real sea test when wrapped in a fishing net, the excellent antifouling performance was demonstrated. The functional hydrogel has great application potential in the protection of seawater-exposed structures, such as bridges and bay ports.