Numerical simulation and experimental verification of fatigue crack propagation in high-strength bolts based on

Ping Zhang1,2, Jiachun Li1, Yu Zhao1

  • 1College of Mechanical Engineering, Guizhou University, Guiyang, China.

Science Progress
|December 7, 2023
PubMed

Keywords:
High-strength boltSIFfatigue crack propagationfatigue testfinite-element analysis

More Related Videos

A Method for Studying the Temperature Dependence of Dynamic Fracture and Fragmentation09:12

A Method for Studying the Temperature Dependence of Dynamic Fracture and Fragmentation

Published on: June 28, 2015

8.6K
Crack Monitoring in Resonance Fatigue Testing of Welded Specimens Using Digital Image Correlation00:05

Crack Monitoring in Resonance Fatigue Testing of Welded Specimens Using Digital Image Correlation

Published on: September 29, 2019

8.3K

Related Concept Videos

Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
185
Fatigue Strength of Concrete01:22

Fatigue Strength of Concrete

Fatigue, in the context of materials science and engineering, refers to the weakening or failure of a material caused by repeatedly applied loads, even if these loads are below the strength limit of the material. Fatigue strength in concrete is a critical property that influences its durability and longevity. Concrete can fail in two ways due to fatigue. Static fatigue or creep rupture occurs under a constant load or one that increases slowly. The other failure mode is due to cyclical or...
194
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
122
Mechanical Characteristics of Steel01:18

Mechanical Characteristics of Steel

The mechanical characteristics of steel are assessed through various tests that evaluate its strength, toughness, and flexibility. These tests include tension, torsion, impact, bending, and hardness assessments, each providing crucial information about steel's suitability for specific applications.
The tension test is fundamental for determining tensile strength. In this test, a steel specimen is stretched using a gripping device until it breaks. The data collected during this test are used...
578
Yield Criteria for Ductile Materials under Plane Stress01:25

Yield Criteria for Ductile Materials under Plane Stress

In designing structural elements and machine parts using ductile materials, it is crucial to ensure that these components withstand applied stresses without yielding. Yielding is initially determined through a tensile test, which evaluates the material's response to uniaxial stress. However, tensile stress is insufficient when components face biaxial or plane stress conditions This condition requires advanced criteria to predict failure.
The Maximum Shearing Stress Criterion, also known as...
165
Design of Columns under a Centric Load01:17

Design of Columns under a Centric Load

The design of columns under centric load is a fundamental aspect of structural engineering and is critical for ensuring the stability and integrity of structures. Euler's and Secant's formulas are central to understanding and calculating the critical load and deformation behaviors of columns, providing a basis for safe and effective structural design.
Euler's formula is applicable under the assumption that the column is a perfect, straight, homogenous prism, and it is operating...
119