Development of nanofibrous scaffolds containing polylactic acid modified with turmeric and hydroxyapatite/vivianite...

Damaging the outer layer of the body (the skin) has been a common issue for decades. Fabrication of nanofibrous membranes via the electrospinning technique for the sake of making the wound healing process more facile has caught a lot of interest. For this purpose, a polymeric scaffold of polylactic acid (PLA) was doped with nanoparticles with different concentrations of turmeric/hydroxyapatite/vivianite/graphene oxide. The obtained membrane was tested by XRD, SEM, FTIR, and XPS. The surface topography of the scaffold has experienced changes upon adding different concentrations of the nanoparticles. The contact angle was measured by water droplets. It accentuated change in CA starting from 43.9^o for pure condition of PLA to 67.7^o for PLA/turmeric/vivianite. The thermogravimetric analysis (TGA) test stated that the PLA scaffold features are thermally stable in relatively high-temperature conditions initiating from room temperature to about 300 °C, meeting the maximum loss in mass of about 5 %. The cell viability was carried out in prepared vitro for the sample which contains PLA/turmeric/vivianite/GO, it was elucidated that the IC₅₀ was around 3060 μg/ml.