Bulk-fill composite in challenging cavities: conversion rate, solubility, and water absorption analysis

In a deep, curved cavity, polymerization of a bulk fill composite can be challenging. The aim of this study was to investigate the solubility, water absorption, and conversion rate of bulk-fill composite samples prepared using molds with various slope angles. Bulk-fill composite resin (Filtek One Bulk Fill) was placed into cylindrical Teflon molds with a depth of 4 mm, angled at varying degrees (90°, 75°, 60°, 45°). Two different LED light-curing units (VALO Cordless, iLed Curing Light) were used to cure the samples. Polymerizations were performed at three different distances (0 mm, 2 mm, and 4 mm). Five samples per group were used, resulting in a total of 24 groups. The Fourier Transform Infrared Spectrometer was utilized to evaluate the conversion levels of the samples. Water sorption and solubility values were determined by storing the composites in distilled water at 37 °C for 21 days. The VALO light-curing unit applied closest to samples inserted in a 90° angulation mold had the highest mean degree of conversion (41.55%), while iLED light-curing unit group that applied from 4 mm to the samples inserted in a 45° angulation mold had the lowest mean conversion (8.97%). The angle of the cavity and the distance at which the light-curing unit is applied significantly affected bulk-fill composite resin conversion. In addition, the choice of light-curing unit impacted the conversion levels. However, with the tested conditions, the water sorption and solubility values of polymerized composite resin samples remain unaffected by these factors.