Hydrogenated TiO₂ Carbon Support for PtRu Anode Catalyst in High-Performance Anion-Exchange Membrane Fuel Cells

The availability of durable, high-performance electrocatalysts for the hydrogen oxidation reaction (HOR) is currently a constraint for anion-exchange membrane fuel cells (AEMFCs). Herein, a rapid microwave-assisted synthesis method is used to develop a core-shell catalyst support based on a hydrogenated TiO₂/carbon for PtRu nanoparticles (NPs). The hydrogenated TiO₂ provides a strong metal-support interaction with the PtRu NPs, which improves the catalyst's oxophilicity and HOR activity compared to commercial PtRu/C and enables greater size control of the catalyst NPs. The as-synthesized PtRu/TiO₂/C-400 electrocatalyst exhibits respectable performance in an AEMFC operated at 80 °C, yielding the highest current density (up to 3× higher) within the catalytic region (compared at 0.80-0.90 V) and voltage efficiency (68%@ 0.5 A cm^-2) values in the compared literature. In addition, the cell demonstrates promising short-term voltage stability with a minor voltage decay of 1.5 mV h^-1. This "first-of-its-kind in alkaline" work may open further research avenues to develop rapid synthesis methods to prepare advanced core-shell metal-oxide/carbon supports for electrocatalysts for use in the next-generation of AEMFCs with potential applicability to the broader electrochemical systems research community.