Novel Perovskite Structured Nd0.5Ba0.5Co1/3Ni1/3Mn1/3O3-δ as Highly Efficient Catalyst for Oxygen Electrode in Solid
Shuang Zhao1, Liwen Huang1, Min Huang2
1Engineering Research Center of Nano-Geo Materials of Ministry of Education, Faculty of Materials Science and Chemistry, China University of Geosciences, No. 388 Lumo Road, Wuhan 430074, China.
Abstract:
Developing catalytic materials with highly efficient oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) is essential for lower-temperature solid oxide fuel cell (SOFC) and electrolysis cell (SOEC) technologies. In this work, a novel triple perovskite material, Nd0.5Ba0.5Co1/3Ni1/3Mn1/3O3-δ, has been developed and employed as a catalyst for both ORR and OER in SOFC and SOEC operations at relatively lower temperatures, showing a low polarization resistance of 0.327 Ω cm2, high-power output of SOFC up to 773 mW cm-2 at 650 °C, and a high current density of 1.57 A cm-2 from SOEC operation at 1.5 V at 600 °C. The relaxation time distribution reveals that Nd0.5Ba0.5Co1/3Ni1/3Mn1/3O3-δ could maintain a slow polarization process at the relatively low operating temperature, offering a significant antipolarization advantage over other perovskite electrode materials. The Nd0.5Ba0.5Co1/3Ni1/3Mn1/3O3-δ electrode provides a low energy barrier of about 0.36 eV in oxygen ion mobility, which is beneficent for oxygen reduction/evolution reaction processes.