Biomass-based controllable morphology of carbon microspheres with multi-layer hollow structure for superior...

The electrochemical properties of corn starch (CS)-based hydrothermal carbon microsphere (CMS) electrode materials for supercapacitor are closely related to their structures. Herein, cetyltrimethyl ammonium bromide (CTAB) was used as a soft template to form the corn starch (CS)-based carbon microspheres with radial hollow structure in the inner and middle layers by hydrothermal and sol-gel method. Due to the introduction of multi-layer hollow structure of carbon microsphere, more micropores were produced during CO₂ activation, which increased the specific surface area and improved the capacitance performance. Compared to commercial activated carbon, the four different morphologies of corn starch CMS had better electrochemical performances. Consequently, the proposed CO₂-(CTAB)-CS-CS exhibits a high discharge specific capacitance of 242.5F/g at 1 A/g in three-electrode system with 6 M KOH electrolyte, better than commercial activated carbon with 208.5F/g. Moreover, excellent stability is achieved for CO₂-(CTAB)-CS-CS with approximately 97.14 % retention of the initial specific capacitance value after 10,000 cycles at a current density of 2 A/g, while the commercial activated carbon has 86.96 % retention. This implies that the corn starch-based multilayer hollow CMS could be a promising electrode material for high-performance supercapacitors.