Development, Characterization, and Antibacterial Analysis of the Selenium-Doped Bio-Glass-Collagen-Gelatin Composite...

Background Guided bone regeneration (GBR) is an often-used technique to aid the successful placement of dental implants in sites with deficient bone. The search for the ideal GBR membrane with bioactive components improving the regenerative outcomes is still on. In this study, a novel composite GBR membrane was developed using selenium-doped bio-glass, collagen, and gelatin. It was further characterized for surface, chemical, biocompatibility, and antibacterial properties. Methodology Selenium-doped bio-glass was prepared using the sol-gel method. The membrane was fabricated using an equal ratio of collagen and gelatin mixed with 1% selenium-doped bio-glass. The solution was poured to obtain a thin layer of the material which was lyophilized to obtain the final GBR membrane. The membrane was analyzed with scanning electron microscopy, energy dispersive X-ray (EDX) analysis, attenuated total reflectance-Fourier transform infrared spectroscopy (ATR-FTIR), zebrafish cytotoxicity test, and antibacterial assay. Results The membrane revealed good surface roughness with lamellar and fibrillar arrangement with a minute granular surface ideal for cell attachment and proliferation. The EDX analysis revealed the presence of carbon, oxygen, and nitrogen as predominant components with trace amounts of calcium, phosphorus, silica, and selenium. Fourier transform infrared spectroscopy analysis also proved the presence of collagen, gelatin, and bio-glass. The membrane revealed excellent biocompatibility with zebrafish growth at a normal rate with 90% viability maintained at 48, 72, and 96 hours and 95% viability at 120 hours. It also exhibited excellent antibacterial activity against Staphylococcus aureus and Escherichia coli with minimal growth of bacterial colonies. Conclusion The developed novel selenium bio-glass collagen and gelatin composite scaffold has a good surface and antibacterial properties along with excellent biocompatibility. Further cell line and in vivo studies should be conducted to explore its role in bone regeneration.